PA66-Functional Nylon 66 Material
Fortune Cat® can produce PA66-Functional Nylon 66 Material.
Item Name: Fortune Cat® PA66-Functional Nylon 66 Material.
Brand: Fortune Cat®
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Product Description
Nylon Raw Textile Material Plants
As the forerunner and leader in China’s nylon industry, Fortune Cat® has been deeply engaged in the field of nylon new materials for more than 40 years and has been the most technologically advanced nylon production enterprise.
Nylon, commonly known as polyamide, is a synthetic fiber. There are many kinds of nylon products, of which nylon 66 industrial filament has high strength, high temperature resistance, fatigue resistance and good impact resistance and other characteristics, is the ideal tire skeleton material. But back in 1977, only a few countries such as the United States and the United Kingdom could produce this material. Under the efforts of the Chinese government, by 1984, China’s annual production of nylon had reached 13,000 tons. By 1997, China had completed the entire process of nylon 66 industrial filament and cord fabric. In 1998, the supporting nylon 66 salt and slicing production line was built successively.
Fortune Cat® is committed to building the nylon 66 industrial filament and tyre fabrics produced in China into a world-renowned brand, closely focusing on the main nylon industry, strengthening and expanding nylon 66, nylon 6 and other related industries and special fiber industries, and building the world’s leading nylon chemical base with scientific and technological innovation and industrial upgrading as a breakthrough. The new project of caprolactam adipate for nylon 66 and nylon 6 products. Among all nylon products, 2100dtex cord fabric, cord fabric for aviation tires, steel wire radial tire fabric, triple ply cord fabric, breaker fabric, polyester cord fabric, nylon 66NN canvas, EP canvas, fine denier nylon 66 technical yarn and other products have been widely recognized by customers at home and abroad. With the continuous growth of production capacity, a large number of projects such as medium and low denier filament, safety airbag filament, succinic acid, caprolactam, and nylon 6 civilian filament, have been completed and put into operation, and Fortune Cat® has entered a rapid development stage.
Nowadays, the annual production of 40000 tons of adiponitrile, 120000 tons of adipodiamine, 30000 tons of nylon 66 chips, 300000 tons of liquid ammonia, and 40000 Nm ³/h. A number of major projects such as hydrogen ammonia projects and dyeing and finishing industrial parks are being accelerated in the construction of new industrial parks. Fortune Cat® has already connected the entire nylon industry chain. Now, a project with an annual production capacity of 30000 tons of nylon 6 civilian nylon filament and an annual production capacity of 130 million meters of high-end nylon fabric has been established, forming a complete industrial chain of caprolactam, nylon 6 polymer chips, nylon 6 civilian filament, weaving, dyeing and finishing. Fortune Cat® produces nearly 400 varieties of nylon product series, extending to a wide range of application fields such as aerospace, military equipment, high-speed rail, clean energy, electronics and appliances, and civil use. Among them, Nylon 66 high-strength ultra-low shrinkage medium low denier industrial filament, spinning grade nylon chip 26HD, high-strength aramid nylon composite dipped tire cord fabric and other products have received unanimous praise from customers.
Fortune Cat® has started the construction of the first phase project with an annual output of 100000 tons of adiponitrile, completely solving the key bottleneck problem that restricts the development of nylon 66; Independently developing nylon 66 dope dye technology, becoming the world’s largest dope-dyed nylon filament production base; Significant progress has been made in the production and application technology of aramid, as well as the research and development of the fourth generation technology of caprolactam. A series of high-end nylon fiber products have been developed, including flame-retardant fibers and ultra-high strength fibers for aviation tires.
Fortune Cat® is committed to building an environmentally friendly enterprise, vigorously promoting the green development of the entire upstream and downstream industry chain. It has successively overcome industry challenges such as twisted yarn collection and waste gas treatment from impregnation, and has achieved rich results in waste heat utilization, clean energy, reclaimed water reuse, low-carbon emission reduction, and other aspects.
E-mail us to get a free quote: fortunecatfibers@outlook.com
PA66-Functional Nylon 66 MaterialFortune Cat® can produce PA66-Functional Nylon 66 Material.
Item Name: Fortune Cat® PA66-Functional Nylon 66 Material.
Brand: Fortune Cat®
Toughened Nylon Material-28EG7S
Characteristics:
Fortune Cat® Toughened Nylon Material-28EG7S is a strengthened and toughened nylon material suitable for making water gauge.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
165 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
210 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
90 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
22 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.34 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
230-245 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
239 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-2725GP
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-2725GP belongs to the category of enhanced red phosphorus flame retardant nylon material, suitable for making electronic and electrical accessories, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
130 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
180 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
60 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
15 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
25 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.20 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
1.0-3.0 |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
— |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
— |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
— |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
V0 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27GF-03
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27GF-03 belongs to enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
125 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
170 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
7 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
55 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
15 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
25 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.2 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
— |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
— |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
— |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state (1.6mm) |
UL94 |
V0 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27GF-02
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27GF-02 belongs to enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
100 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
140 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
34 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
10 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
16 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.2 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
— |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
— |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
|
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
|
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
V0 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27GF-01B
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27GF-01B belongs to black enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
110 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
135 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
45 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
12 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
15 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.2 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
— |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
— |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1.7*1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
V0 |
||
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27F-01
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27F-01 belongs to white enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
75 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
110 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3.6 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
70 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
10 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.1 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
235-250 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
75 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
8.9×1015 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state (1.6mm) |
UL94 |
V1 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27F-01B
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27F-01B belongs to Black enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
80 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
15 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
50 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
150 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
8 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.1 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
253-259 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
75 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
17 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
8.9*1013 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
V0 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Flame Retardant Nylon Material-27F-03
Characteristics:
Fortune Cat® Flame Retardant Nylon Material-27F-03 belongs to white enhanced flame retardant nylon material, suitable for making electrical switch boxes, electronic connectors, mechanism seats, etc.
How To Use:
Dry at 80-90 ℃ for 8-12 hours before use.
Injection temperature: 260~270 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
80 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
9 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
110 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3.3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
80 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
10 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.1 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
235-250 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
75 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
8.9*1015 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state (1.6mm) |
UL94 |
V0 |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Toughened Nylon Material-ST808
Characteristics:
Fortune Cat® Toughened Nylon Material-ST808 is suitable for making van accessories, etc.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
60 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
27 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
60 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
1.0 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
No damage |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
60 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.12 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
241-253 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
70 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
|
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
— |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Toughened Nylon Material-ST003
Characteristics:
Fortune Cat® Toughened Nylon Material-ST003 is suitable for making railway wear-resistant board, toys, etc. It has low temperature resistance and excellent impact resistance.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (Dry state) |
ISO527 |
70 |
MPa |
|
Elongation at break |
23℃ (Dry state) |
ISO527 |
20 |
% |
|
|
Bending strength |
23℃ (Dry state) |
ISO178 |
75 |
MPa |
|
|
Flexural modulus |
23℃ (Dry state) |
ISO178 |
1.2 |
GPa |
|
|
Non-notched impact strength |
23℃ (Dry state) |
ISO179 |
No damage |
KJ/m2 |
|
|
Notch impact strength |
23℃ (Dry state) |
ISO179 |
40 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.16 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
1.5-3.0 |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
— |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
78 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Toughened Nylon Material-2703T
Characteristics:
Fortune Cat® Toughened Nylon Material-2703T is suitable for making railway baffle seat, pipe fittings, sports equipment,etc. It has low temperature resistance and high impact resistance.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (Dry state) |
ISO527 |
55 |
MPa |
|
Elongation at break |
23℃ (Dry state) |
ISO527 |
30 |
% |
|
|
Bending strength |
23℃ (Dry state) |
ISO178 |
75 |
MPa |
|
|
Flexural modulus |
23℃ (Dry state) |
ISO178 |
1.2 |
GPa |
|
|
Non-notched impact strength |
23℃ (Dry state) |
ISO179 |
No damage |
KJ/m2 |
|
|
Notch impact strength |
23℃ (Dry state) |
ISO179 |
75 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.15 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
240-260 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
78 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
— |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
— |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Toughened Nylon Material-2703TL
Characteristics:
Fortune Cat® Toughened Nylon Material-2703TL is suitable for making toys, sports equipment, sports equipment, bearing sleeves, etc. It has low temperature resistance, aging resistance, and high impact resistance.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
55 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
46 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
60 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
1.0 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
No damage |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
60 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.12 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
253-257 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
73 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
— |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
— |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Toughened Nylon Material-2141TT
Characteristics:
Fortune Cat® Toughened Nylon Material-2141TT is suitable for making railway products, etc. It has excellent low-temperature resistance and impact resistance.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
45 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
75 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
52 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
1.0 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
No damage |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
110 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.12 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
241-253 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
— |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
— |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
— |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-HW-46
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-HW-46 is suitable for making high speed railway products, etc.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
180 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
235 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
115 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
25 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
34 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.39 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
255-265 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
22 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-BHW-47
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-BHW-47 is black, suitable for making van accessories, etc.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
155 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7.0 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
190 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
4.5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
90 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
20 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
32.5 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.36 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
255-265 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
22 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1.7×1015 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-2107H
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-2107H is suitable for making railway products, etc.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
160 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
205 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
90 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
23 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
35 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.41 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-258 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
238 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
21 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1.7×1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
— |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-2106H
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-2106H is suitable for making railway products,sports equipment, etc.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
160 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
205 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
90 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
23 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
30 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.34 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-258 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
240 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
21 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-L2730G
Characteristics:
Fortune Cat® Strengthened Nylon Material-L2730G is suitable for making mechanical cover, fan blades, gears, coil framework, machine tool accessories, etc. It is PA66+33% fiberglass reinforced products have excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~280 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
||
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
190 |
MPa |
|
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6 |
% |
||
|
Modulus of elasticity for tension |
23℃ (dry state) |
ISO527 |
10 |
GPa |
||
|
Bending strength |
23℃ (dry state) |
ISO178 |
290 |
MPa |
||
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
8 |
GPa |
||
|
Simply supported beam |
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
105 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
20 |
KJ/m2 |
||
|
Notch impact strength of cantilever |
23℃ (dry state) |
ISO180 |
20 |
KJ/m2 |
||
|
Glass fiber content |
Dry state |
ISO3451 |
33 |
% |
||
|
Physical performance
|
Melt flow rate |
Dry state |
ISO1133 |
23 |
g.10min-1 |
|
|
Molding shrinkage |
Parallel |
ISO294 |
Slightly inflated |
|
||
|
Vertical |
0.50 |
|
||||
|
Rockwell hardness |
L |
ISO2039 |
106 |
|
||
|
M |
95 |
|
||||
|
R |
115 |
|
||||
|
Thermal performance |
Melting point |
Dry state |
ISO11357 |
265 |
℃ |
|
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
254 |
℃ |
||
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-L2730GH
Characteristics:
Fortune Cat® Strengthened Nylon Material-L2730GH is suitable for making Mechanical covers, blades, gears, and peripheral components of automotive engines, etc. It is PA66+33% fiberglass reinforced product, with excellent mechanical properties and dimensional stability, and good heat resistance.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~280 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
||
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
190 |
MPa |
|
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6.5 |
% |
||
|
Modulus of elasticity for tension |
23℃ (dry state) |
ISO527 |
10 |
GPa |
||
|
Bending strength |
23℃ (dry state) |
ISO178 |
290 |
MPa |
||
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
8 |
GPa |
||
|
Simply supported beam |
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
105 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
20 |
KJ/m2 |
||
|
Notch impact strength of cantilever |
23℃ (dry state) |
ISO180 |
20 |
KJ/m2 |
||
|
Glass fiber content |
Dry state |
ISO3451 |
33 |
% |
||
|
Physical performance
|
Melt flow rate |
Dry state |
ISO1133 |
20 |
g.10min-1 |
|
|
Molding shrinkage |
Parallel |
ISO294 |
0.25 |
|
||
|
Vertical |
0.50 |
|
||||
|
Rockwell hardness |
L |
ISO2039 |
120 |
|
||
|
M |
95 |
|
||||
|
R |
110 |
|
||||
|
Thermal performance |
Melting point |
Dry state |
ISO11357 |
265 |
℃ |
|
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
255 |
℃ |
||
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2750G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2750G is widely used in automotive industry, electric tool components, transportation, military products, high-speed gears, and construction. It is PA66+50% fiberglass reinforced products have excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
230 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
300 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
8 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
110 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
25 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
50 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.45 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
255-265 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
247 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
23 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2730G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2730G is suitable for making mechanical cover, fan blades, gears, coil framework, machine tool accessories, etc. It is PA66+30% fiberglass reinforced product, with excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~280 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
175 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
210 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
105 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
25 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
30 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.35 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-260 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
250 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
18 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-KZ02
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-KZ02 is suitable for making railway products, etc. It has excellent low temperature resistance, impact resistance, and excellent tensile performance.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 70-100MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
175 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
9 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
215 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
4.5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
110 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
27 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
— |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.32 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
1.0-1.5 |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
255-260 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
22 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2730GB
Characteristics:
Fortune Cat® Strengthened Nylon Material-2730GB is suitable for making mechanical cover, fan blades, gears, coil framework, machine tool accessories, etc. It is PA66+30% fiberglass reinforced black product with excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~280 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
155 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
200 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
60 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
15 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
30.0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.35 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-260 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
17 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened and Toughened Nylon Material-HW-47
Characteristics:
Fortune Cat® Strengthened and Toughened Nylon Material-HW-47 is suitable for making high-speed railway products, etc. It has excellent low temperature resistance and excellent impact resistance.
How To Use:
Dry at 80-110 ℃ for 8-12 hours before use.
Injection temperature: 270~295 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
175 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
9 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
220 |
MPa |
|
|
Flexural modulus |
23℃ (Dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
110 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
27 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
32.5 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.36 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
255-265 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
22 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2720G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2720H is suitable for making medium rigid mechanical components, shields, and electrical insulation products, etc. It is PA66+20% fiberglass reinforced products have excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
150 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
9 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
180 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
65 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
16 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
20 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.27 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-258 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
21 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
7.8×1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
|
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2710G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2710G is suitable for making medium strength mechanical components, shields, plastic brackets, etc. It is PA66+10% GF. Has excellent dimensional stability and fluidity.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
105 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
130 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
2 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
40 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
10 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
10 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.18 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
257-262 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2130G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2130G is suitable for making mechanical cover, fan blades, gears, coil framework, machine tool accessories, etc. It is PA66+30% fiberglass reinforced black product with excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 270~280 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
150 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
180 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
4 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
45 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
12 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
30.0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.35 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-256 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
247 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2120G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2120G is suitable for making medium rigid mechanical components, shields, and electrical insulation products, etc. It is PA66+20% fiberglass reinforced products have excellent mechanical properties and dimensional stability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
140 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
185 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
50 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
16 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
20 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.27 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
245-258 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-2110G
Characteristics:
Fortune Cat® Strengthened Nylon Material-2110G is suitable for making medium rigid mechanical components, gears, plastic brackets, etc. It is PA66+10% GF. has excellent dimensional stability and good fluidity.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 260~275 ℃
Injection speed: medium fast
Injection pressure: 60-80MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
| Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
90 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
6 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
130 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
2 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
40 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
10 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
10 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.18 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
— |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
257-262 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
245 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
— |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1014 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
— |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
|
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-B2730G
Characteristics:
Fortune Cat® Strengthened Nylon Material-B2730G is suitable for making mechanical guards, blades, gears, electric tools, etc. It is PA6+30% fiberglass reinforced products have excellent mechanical properties and processability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 230~250 ℃
Injection speed: medium fast
Injection pressure: 60-70MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
175 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
220 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
105 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
22 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
30.0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.36 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
—- |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
225-255 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
215 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
20 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1013 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
1.25 |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-B2718G
Characteristics:
Fortune Cat® Strengthened Nylon Material-B2718G is suitable for making mechanical covers, blades, gears, and electric tools, etc. It is PA6+18% fiberglass reinforced products have excellent mechanical properties and processability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 230~250 ℃
Injection speed: medium fast
Injection pressure: 60-70MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance
|
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (Dry state) |
ISO527 |
140 |
MPa |
|
Elongation at break |
23℃ (Dry state) |
ISO527 |
8 |
% |
|
|
Bending strength |
23℃ (Dry state) |
ISO178 |
160 |
MPa |
|
|
Flexural modulus |
23℃ (Dry state) |
ISO178 |
4.5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
85 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
15 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
18.0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.25 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
—- |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
225-255 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
210 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
20 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1013 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
1.25 |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Strengthened Nylon Material-B2710G
Characteristics:
Fortune Cat® Strengthened Nylon Material-B2710G is suitable for making Mechanical covers, blades, gears, and electric tools, etc. It is PA6+10% fiberglass reinforced products have excellent mechanical properties and processability.
How To Use:
Dry at 80-100 ℃ for 8-12 hours before use.
Injection temperature: 230~250 ℃
Injection speed: medium fast
Injection pressure: 60-70MPa
Injection cycle: determined based on the thickness of the workpiece
Mold temperature: 60-80 ℃
The following table shows typical value of this product. Please consult our material engineers about specific usage.
|
Item performance |
Test condition |
Test method |
Test data |
Data unit |
|
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
90 |
MPa |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
7.5 |
% |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
120 |
MPa |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
3.5 |
GPa |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
50 |
KJ/m2 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
8 |
KJ/m2 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
10.0 |
% |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
1.20 |
g/cm3 |
|
Molding shrinkage |
Dry state |
|
—- |
% |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
225-255 |
℃ |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
210 |
℃ |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
20 |
MV/m |
|
Volume resistivity |
Dry state |
GB/T1410 |
1013 |
Ω.cm |
|
|
Other |
Water absorption |
|
|
1.25 |
% |
|
Flame retardant property |
Dry state |
UL94 |
HB |
— |
|
If you are interested in this product, please feel free to contact us: fortunecatfibers@outlook.com
Address:
International Sales Department
Fortune Cat® Fibers
Jinduhuafu 6#4#308, Jianping, Chaoyang, Liaoning, China.
E-mail: FortuneCatFibers@outlook.com