Carbon Fiber

Carbon Fiber

Fortune Cat® can produce Carbon Fiber.

Item Name: Carbon Fiber.

Brand: Fortune Cat®

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

Product Description

Carbon Fiber Plants

Fortune Cat® Carbon Fiber Production Base specializes in the research and development, as well as production, of PAN-based carbon fiber precursor, carbon fiber filaments, carbon fiber composite materials, and carbon fiber products. Fortune Cat® can provide customers with integrated full industry chain services, including carbon fiber precursor, carbon fiber filaments, carbon fiber fabrics, liquid resins, adhesives, carbon fiber prepreg, carbon fiber composite components, and aviation composite structural components. The production capacity can reach 40000 tons of carbon fiber precursor and 20000 tons of large tow carbon fiber per year. By testing, the 48K carbon fiber produced by the Fortune Cat® carbon fiber production base has a tensile strength of 4000Mpa, a tensile modulus of 240Gpa, and an interlayer shear strength of 60Mpa.

PAN based carbon fibers can be divided into small and large fiber tows according to fiber tow size. Fiber tows below 24k refer to small tow carbon fiber, which consist of 1000-24000 individual fibers; And the specification of large tow carbon fiber is ≥ 48k, which means that the number of single fibers in the bundle exceeds 48000. In addition to distinguishing between simple tow specifications, there are significant differences in mechanical properties and application fields between small and large tow carbon fibers.

Small tow carbon fiber has excellent mechanical properties, with a tensile strength of 3.5-7.0 GPa and a tensile modulus of 230-650 GPa. It is mainly used in aerospace, defense and military industries, as well as high-end sports and leisure products, and is therefore also known as aerospace grade carbon fiber. Aerospace grade small fiber tows have extremely strict requirements for reliability, processability, stability, and so on.

Large tow carbon fibers have a tensile strength of 3.5-5.0 GPa and a tensile modulus of 230-290 GPa, and are generally used in fields such as textiles, medicine and health, electromechanical, civil engineering, transportation, and energy, hence they are also known as industrial grade carbon fibers. The technical barriers for large tow carbon fiber are quite high. As an industrial grade carbon fiber, its core driving force lies in low cost, so enterprises must effectively control production costs. The rapidly growing global wind power industry has brought business opportunities for the development of Fortune Cat®‘s large tow carbon fiber.

In the subsequent application process of large tow carbon fiber, due to the large size and easy aggregation of fiber bundles, the yarn spreading effect is not good, which leads to poor resin infiltration into the fibers and is prone to defects such as pores. In addition, during the process of developing large tow carbon fibers, there may be disordered and broken yarns, resulting in significant dispersion of mechanical properties, further increasing the difficulty of applying large tow carbon fibers.

In the medical field, carbon materials have advantages such as good biocompatibility, low irritation to living tissues, non-toxic, non-carcinogenic, low specific gravity, and similar elastic modulus to human bone, making them a potential fourth generation implant material.

In the field of transportation, the application of large tow carbon fiber is mainly in civil aircraft, automobiles, fast trains, and other transportation vehicles. For example, it can be used to manufacture carbon/carbon composite brake systems and automotive transmission shafts, which can significantly reduce the weight of automobiles, thereby reducing energy consumption and improving automotive control systems, which is beneficial for environmental protection and has become the preferred choice for automotive lightweighting.

Carbon fiber has broad application prospects in the energy field. At present, in the field of energy, carbon fiber reinforced composite materials mainly solve two problems. Firstly, improving energy utilization efficiency. For example, carbon fiber used in automotive components can reduce vehicle weight and improve fuel utilization efficiency; The second is to provide clean energy, such as carbon fiber wind turbine blades and carbon fiber wind turbine propellers applied in the wind power field.

In the field of sports and leisure, large tow carbon fiber products mainly include fishing rods, golf clubs, snowboards, badminton rackets, etc.

In terms of infrastructure, large tow carbon fibers can be used to enhance cement. Carbon fiber reinforced cement composite materials have high strength and stiffness, and can be applied in bridges, buildings, and other fields to further increase the service life of buildings.

In the industrial field, carbon fiber can be applied in industries such as papermaking, metallurgy, chemical, textile, and medical machinery. Various components that require working in environments such as high strength, high stiffness, light weight, high temperature resistance, and corrosion resistance, such as various shafts, containers, pipelines, and platforms, can be manufactured using carbon fiber.

Fortune Cat®’s products mainly include carbon fiber basic materials, high-strength carbon fibers, carbon fiber fabrics, high-performance material fabrics, warp knitted reinforced fabrics, multi axial warp knitted composite materials, advanced carbon fiber composite materials for rail transit, multiple models of high-speed trains, carbon fiber composite material components for maglev trains and aerospace, high-performance prepregs, carbon fiber composite material products, etc. Fortune Cat®’s carbon fiber product is widely used in aerospace, weapons and equipment, wind turbine blades, photovoltaic thermal fields, high-pressure hydrogen storage, sports and leisure, building reinforcement and other fields.

E-mail us to get a free quote: fortunecatfibers@outlook.com

Carbon Fiber

Fortune Cat® can produce Carbon Fiber.

Item Name: Carbon Fiber.

Brand: Fortune Cat®

PAN based 1K carbon fiber

Carbon fiber has the characteristics of low specific gravity, high specific strength, high specific modulus, low thermal conductivity, small thermal expansion coefficient (stable size), resistance to ablation, and good self-lubricating properties. At the same time, it also has the flexibility of fibers and can be woven, processed, and wound into shape. It can be used as a corrosion-resistant material, structural material, and raw material for heating elements. It is widely used in industrial production, aerospace, sports equipment, and other civilian production.

Tensile strength (Gpa) ≥ 3.0

Modulus (Gpa) 210-240

Density (g/cm3) 1.76

Carbon content (%) ≥ 93

Elongation rate (%) ≥ 1.5

Diameter( μ) 6-8

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

PAN based 3K carbon fiber

Tensile strength (Gpa) ≥ 3.0

Modulus (Gpa) 210-240

Density (g/cm3) 1.76

Carbon content (%) ≥ 93

Elongation rate (%) ≥ 1.5

Diameter( μ) 6-8

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

PAN based 6K carbon fiber

Tensile strength (Gpa) ≥ 3.0

Modulus (Gpa) 210-240

Density (g/cm3) 1.76

Carbon content (%) ≥ 93

Elongation rate (%) ≥ 1.5

Diameter( μ) 6-8

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

PAN based 12K carbon fiber

Tensile strength (Gpa) ≥ 3.0

Modulus (Gpa) 210-240

Density (g/cm3) 1.76

Carbon content (%) ≥ 93

Elongation rate (%) ≥ 1.5

Diameter( μ) 6-8

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

PAN based carbon fiber cloth

Carbon fiber cloth is woven from polyacrylonitrile based carbon fibers and can be used together with carbon felt as insulation material for vacuum electric furnaces. It can also be used as a reinforcing material for C/C composite materials and as a reinforcement material for bridges.

Specification 1K 3K 6K 12K
Warp and weft density (Number/25mm) 28 ± 2 21 ± 2 16 ± 2 11 ± 2
Thickness (mm) 0.15 ± 0.02 0.28 ± 0.02 0.4 ± 0.02 0.5 ± 0.02
Warp Tensile Strength (N) 500 800 1200 1400
Weft Tensile Strength (N) 400 600 1000 1200

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

Viscose-based carbon fibre

Tensile strength (MPa) ≥200
Carbon content % ≥90
Specific gravity (g/cm3) 1.6—1.65
Length (mm) ≥500
Impurity No

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

Chopped carbon fiber

Density(g/cm3) ≥ 1.76
Carbon Content % ≥93
Specifications 1mm,3mm,5mm/made to order

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com

Carbon fiber powder

Carbon fiber powder is a short cut carbon fiber made by mechanically grinding carbon fibers. It has conductivity and can be used as a reinforcing material for resins. It has dimensional stability and is suitable for automatic feeding and metering extrusion processes. It has been widely used in electronic chips, conductive boards, conductive flooring, electronic machinery chassis, etc.

Carbon Content % ≥93
Volume Density(g/L) ≥ 300
Moisture Content <0.3%

If you are interested in this product, please feel free to contact us: fortunecatyarns@outlook.com